…8% Co2 100% CO2 may produce lower quality arc conditions Gas Flow Rate: 20-60 CFH Hardness: 49-54 HRC Shielding Gases: 100% Argon Gas Flow Rate: 20-40 CFH Description: WT H-13…
…8% Co2 100% CO2 may produce lower quality arc conditions Gas Flow Rate: 20-60 CFH Hardness: 49-54 HRC Shielding Gases: 100% Argon Gas Flow Rate: 20-40 CFH Description: WT H-13…
…rods are designed to obtain microscopic clean weld deposits. Chemical Composition (Wt%): C Mn Cr Si Mo 0.35 0.30 1.70 0.50 0.40 Note: Single values are maximum unless otherwise noted….
…to high impact loading. Buildup/joining Mn steel to Mn steel. Weldman 3 High chromium, high manganese alloy used in the rebuilding of manganese parts subject to severe impact loading. Buildup/joining…
…DC straight or reverse polarity. It has poor machinability, no surface checks, high impact resistance and fair abrasive resistance. Contains: carbon, silicon, nickel, chromium, manganese Chemical Composition: View/Download Data Sheet…
…those involving high temperature service, are adversely affected if the ferrite content is too high. Consequently, a high-ferrite content should not be specified unless tests prove it to be absolutely…
…the manufacture of gas turbine components. Ti-6-2-4-2 has high temperature stability for long term applications up to 1000°F. In its sheet metal form, this alloy is often used in engine…
…in a variety of alloys, such as silver, gold, copper, etc. They range in thicknesses up to 0.003 in. Brazing Rope Weldtool brazing rope is a highly flexible, dry brazing…
…is less sensitive to the heating rate and therefore should not separate into low/high melting constituents. Ag: 50% | Cd: 18% | Zn: 16.5% | Cu: 15.5% View/Download Data Sheet…
…heating rate and therefore should not separate into low/high melting constituents. With this metal, in some instances special fluxes may be needed for optimum bonding and wetting. View/Download Data Sheet…
…this filler metal is less sensitive to the heating rate and therefore should not separate into low/high melting constituents. With this metal, in some instances special fluxes may be needed…